P-20 is a plastic mould steel.It is a pre-hardened material with uniform hardness. Three grades of P20 are :- Din 1.2311, Din 1.2738, P20 Steel High Hard.

P-20 Steel (1.2311)
We Are Leading Plastic Mould Steel DIN 1.2311,P20 Steel and Mould Steel traders & Suppliers in Delhi. We are supplier and trader of wide range of Plastic Mould Steel DIN 1.2311 or Pre Hard Plastic Mould Steel. All our plastic mould making steel grades are produced with special types of chemical composition and production process. At the mill it allows to the steel to maintain a good mechanical properties for small size Plastic Mould, medium Plastic Mould and large Plastic Mould making. We are engaged in offering a very wide range of Plastic Mould Steel P20 Grade. These Steel applications are there in various industries like Plastic injection moulds, petrochemical Industry and many more other Industries. Moreover These Steel products are produced by our quality vendors by using high grade of raw materials and with advanced technology and Process.

P-20 Steel (1.2738) (P20+Ni)
We are a globally applauded P20 Steel 1.2738 and P20 PLASTIC MOULD STEEL, suppliers Delhi India. We are providing you the best range of Plastic Mold, Steel plate and p20 steel plate with effective & timely delivery. We offer a very low P20 steel price per kg in India. We are engaged in offering a very wide range of Plastic Mould Steel P20 Grade. These Steel applications are there in various industries like Plastic injection moulds, petrochemical and others, these Steel products are produced by our vendors using a high grade raw materials and with advanced technology and Process.


P20 Steel High Hard
High Hardness Steel P20 – HRC 40

We are Supplying High Hardness Steel P20 HRC 40 for Plastic Moulds. We have High Hardness Steel HRC 40 Plastic Mould Steel, P20 Grade 1.2738, P20 Steel 1.2311 and 1.2316 in ready stock.

We Supplying High Hardness Steel P20, HRC 40 for Plastic Moulds making. We have in stock High Hardness Steel P20 Steel Plates in all sizes. HRC 40 Plastic Mould Steel best for production tools making.

Preheating : As P20 is sold in a pre-hardened position, hardening heat treatment is not needed. After machining and intermittently during pottery, the steel must be thermally stress relieved by heating to 900F (482C), equalizing and holding for one hour per inch (25.4mm) of width, and cooling in air to ambient heat.

In those rare circumstances where the steel must be re-hardened, the steel must first be annealed prior to solidification.

Austenitizing (High Heat) : Heat rapidly from the preheat to 1550F (843C). Soak for 30 minutes for first inch (25.4mm) of breadth, plus 15 minutes for each additional inch (25.4mm).

Quenching : Pressurized gas, or interrupted oil to 150-125ºF (66-51ºC).
For oil, quench until black, at about 900°F (482°C), then cool in still air to 150-125°F (66-51°C).

Tempering : Temper immediately after quenching or cryogenic method. Hold at the temperature for 1 hour per inch (25.4mm) of density, 2 hours particle, then air cool to ambient heat. Tempering temperatures and hardness are given in chart over.